HF 00652E
HF00652E is a bimodal high density polyethylene blown film resin with high molecular weight. It provides high impact and toughness properties as well as very good stiffness.
HF00652E is a bimodal high density polyethylene blown film resin with high molecular weight. It provides high impact and toughness properties as well as very good stiffness.
Applications:
Blown film, Merchandise bags and Grocery bags.
Technical properties :
| Resin Properties | English | SI | Test Based On |
| Density |
0.952 g/cm3
|
0.952 g/cm3 | Manufacturer Method |
| Melt Index, 190⁰ C/2.16 kg |
0.06 g/10 min
|
0.06 g/10 min | ASTM D1238 |
| Tensile Strength at Yield MD |
5500 psi
|
38 MPa
|
ASTM D882 |
| Tensile Strength at Yield TD |
4800 psi
|
33 MPa | ASTM D882 |
| Elongation at break MD | 270 % | 270 % | ASTM D882 |
| Elongation at break TD | 380 % | 380 % | ASTM D882 |
| Secant Modulus MD 1% Secant | 150000 psi | 1100 Mpa | ASTM D882 |
| Secant Modulus TD 1% Secant | 160000 psi | 1100 Mpa | ASTM D882 |
| Peak Melting Temperature | 267 °F |
130 °C
|
Manufacturer Method |
| Dart Drop Impact |
300 g
|
300 g
|
ASTM D1709A |
Storage and handling:
Emeraude HDPE HF00652E resin is considered stable under normal ambient and anticipated storage and
handling conditions. This material should be stored in a dry cool place with adequate ventilation and
protected from UVlight at temperature below 50°C. Please refer to our Material Safety Data Sheet to get
additional information.