F01552
SABIC HDPE F01552 is a medium molecular weight High Density Polyethylene specifically designed for blown film extrusion. It has a broad molecular weight with excellent extrudability， high film strength and draw down characteristics. The material contains anti oxidant.
SABIC HDPE F01552 is a medium molecular weight High Density Polyethylene specifically designed for blown film extrusion. It has a broad molecular weight with excellent extrudability， high film strength and draw down characteristics. The material contains anti oxidant.
Applications:
SABIC® HDPE F01552 resin is recommended for the production of strong millinery and notion bags, deep freeze bags, table cloths and thin film as quality
replacement for paper products.
Technical properties :
| Resin Properties | Typical value | Test Based On |
| Melt Index, 190⁰ C/2.16 kg |
0.15 g/10 min
|
ISO 1133 |
| Melt Index, 190⁰ C/21.6 kg | 16 g/10 min | ISO 1133 |
| Density | 952 kg/m3 | ASTM D1505 |
| stress at break, MD | 55 Mpa | ASTM D882 |
| stress at break, TD | 49 Mpa | ASTM D882 |
| strain at break, MD | 400 % | ASTM D882 |
| strain at break, TD | 610 % | ASTM D882 |
| stress at yield, MD | 31 Mpa | ASTM D882 |
| stress at yield, TD | 30 Mpa | ASTM D882 |
| 1% secant modulus, MD | 1400 Mpa | ASTM D882 |
| 1% secant modulus, TD | 1700 Mpa | ASTM D882 |
| Elmendorf Tear Strength MD | 4 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 40 g | ASTM D1922 |
| Dart Impact Strength F50 | 180 g | ASTM D1709 |
| Vicat Softening Temperature | 125 C° | ASTM D1525 |