HP 456J
Moplen HP456J is a polypropylene homopolymer used for extrusion and thermoforming applications. Moplen HP456J is formulated with a low water-carry-over additive package. Typical applications are monofilaments, ropes and tapes.
APPLICATIONS :
Intermediate Bulk Containers; Raffia/Tapes/Strapping
PROCESSING METHOD :
Tapes & Raffia
TYPICAL PROPERTIES:
| TYPICAL PROPERTIES | UNIT | VALUE | TEST METHOD |
| Melt Flow Rate, (230 °C/2.16 kg) | g/10 min | 3.4 | ISO 1133-1 |
| Density | g/cm3 | 0.900 | ISO 1183-1 |
MECHANICAL PROPERTIES:
| DESCRIPTION OF PROPERTIES | UNIT | VALUE | TEST METHOD |
| Flexural Modulus Tensile Stress at Break, (23 °C, 50 mm/min) Tensile Stress at Yield, (23 °C, 50 mm/min) Tensile Strain at Break, (23 °C, 50 mm/min) Tensile Strain at Yield, (23 °C, 50 mm/min) |
N/mm² N/mm² N/mm² % % |
1500 21 34 200 11 |
ISO 178 ISO 527-1, -2 ISO 527-1, -2 ISO 527-1, -2 ISO 527-1, -2 |
THERMAL :
| DESCRIPTION OF PROPERTIES | UNIT | VALUE | TEST METHOD |
| Vicat Softening Temperature, (A50) | C° | 156 | ISO 306 |
| Deflection Temperature Under Load, (0.45 MPa, Unannealed) | C° | 91 | ISO 75B-1, -2 |
Storage:
The resin is packed in 25 kg bags, octabins or bulk containers protecting it from contamination. If it is stored under certain conditions, i. e. if there are large fluctuations in ambient temperature and the atmospheric humidity is high, moisture may condense inside the packaging. Under these circumstances, it is recommended to dry the resin before use. Unfavorable storage conditions may also intensify the resin’s slight characteristic odor.
Resin should be protected from direct sunlight, temperatures above 40°C and high atmospheric humidity during storage. Higher storage temperatures may reduce the storage time.