LL 1001 BU

ExxonMobil™ LL 1001BU resin offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1001BU resin.

APPLICATIONS:
Agricultural Film, Bag in Box, Barrier Food Packaging, Blown Film, Bread Bags, Food Packaging, Form Fill And Seal Packaging, Freezer Film, Garment Film, General Packaging, Heavy Duty Bag, Ice Bags, Industrial Liners, Industrial Packaging, Lamination Film, Liners, Multilayer Packaging Film, Packaging Films, Produce Bags, Refuse Bags, Shoppers, Stand Up Pouches, Trash Bags

Resin properties :

Resin Properties	Typical Value	Test Based On
Density	0.918 g/cm³	ASTM D1505
Melt Index (190°C/2.16 kg)	1.0 g/10 min	ASTM D1238
Peak Melting Temperature	122 C°	ExxonMobil Method

Thermal :

Thermal	Typical Value (English)	Typical Value (SI)	Test Based On
Vicat Softening Temperature	207 °F	97 °C	ASTM D1525

Film properties :

Molded Properties	Typical Value	Test Based On
Tensil Strenght at Yield MD	9.3 Mpa	ASTM D882
Tensil Strenght at Yield TD	9.7 Mpa	ASTM D882
Tensil Strenght at Break MD	44 MPa	ASTM D882
Tensil Strenght at Break TD	26 MPa	ASTM D882
Elongation at Break MD	510 %	ASTM D882
Elongation at Break TD	690 %	ASTM D882
Secant Modulus MD – 1% Secant	170 MPa	ASTM D882
Secant Modulus TD – 1% Secant	190 MPa	ASTM D882
Dart Drop Impact	80 g	ASTM D1709A
Elmendorf Tear Strength MD	100 g	ASTM D1922
Elmendorf Tear Strength TD	450 g	ASTM D1922
Poncture force	26 N	ExxonMobil Method
Poncture Energy	1.1 J	ExxonMobil Method

Optical Properties :

	Typical Value (SI)	Test Based On
Gloss (45°)	53	ASTM D2457
Haze	13 %	ASTM D1003